| Property | Nominal Property Data | Part Number | Applicable Instrument Models |
| PARTICLE SIZE | Garnet Powder (15 g) | 004-16811-00 | 5000, 5000D, 5000E, 5000ET, 5100, 5120 |
| Mass Median Diameter ≈ 11.6 µm | |||
| Glass Powder (15 g) | 004-16814-00 | ||
| Mass Median Diameter ≈ 1.7 µm | |||
| Calcium Carbonate Powder (28 g) | 004-16835-00 | ||
| Mass Median Diameter ≈ 0.77 µm | |||
| (traceable to N. I. S.T.) | |||
| Garnet Powder (20 g) | 004-16837-00 | ||
| Mass Median Diameter ≈ 3.77 µm | |||
| (traceable to N .I .S. T.) | |||
| Garnet Powder (1 g) | 004-16841-00 | 5200, 5205 | |
| Volume Median Spherical Diameter ≈ 4.85 µm | |||
| (traceable to N. I. S. T.) | |||
| Monosize Polymer Microspheres (7 mL) | - | 5380, 5382, 5390 | |
| Nominal Diameter ≈ 1 µm | 004-16840-00 | ||
| Nominal Diameter ≈ 2 µm | 004-16840-01 | ||
| Nominal Diameter ≈ 3 µm | 004-16840-02 | ||
| Nominal Diameter ≈ 5 µm | 004-16840-03 | ||
| Nominal Diameter ≈ 10 µm | 004-16840-04 | ||
| Nominal Diameter ≈ 20 µm | 004-16840-05 | ||
| Nominal Diameter ≈ 40 µm | 004-16840-06 | ||
| Nominal Diameter ≈ 100 µm | 004-16840-08 | ||
| MERCURY POROSIMETRY | Silica Alumina (15 g) | 004-16822-00 | 9200, 9210, 9220, 9300, 9305, 9310, 9320, 9400, 9405, 9410, 9420, 9500, 9505, 9510, 9520 |
| Average Pore Diameter ≈ 0.0073 µm Pore Volume ≈ 0.56 cm3/g | |||
| MICROPORE | 13X Molecular Sieve (10 g) | 004-16826-00 | 2000 Micropore 2010 Micropore |
| Pore Size ≈ 10.5 Å using Ar adsorbate | |||
| Pore Size ≈ 14 Å using CO2 adsorbate | |||
| Pore Size ≈ 8.3 Å using N2 adsorbate | |||
| 13X Molecular Sieve (10 g) | 004-16843-00 | 2020 Micropore | |
| Pore Size ≈ 10.5 Å using Ar adsorbate | |||
| Pore Size ≈ 14 Å using CO2 adsorbate | |||
| Pore Size ≈ 8.3 Å using N2 adsorbate | |||
| Y-Zeolite (2.5 g) | 004-16844-00 | 2020 Micropore | |
| Pore Size ≈ 7.4 Å using Ar adsorbate | |||
| Pore Size ≈ 7.4 Å using N2 adsorbate | |||
| ZETA POTENTIAL | Kaolinite (120 g) | 004-16824-00 | 1202 |
| Mean Zeta Potential = -60 mV | |||
| CHEMISORPTION | Platinum Alumina Pellets (5 g) | 004-16825-00 | 2000, 2010, 2020, 2700, 2705, 2800, 2810, 2900, 2910, 2920, 2950 |
| Active Metal Dispersion: | |||
| ≈ 39.9%, 2000 and 2010 | |||
| ≈ 48.6%, all others | |||
| Silver Oxide (2 g) | 004-16836-00 | 2700, 2705, 2900, 2910, 2920,2950 | |
| Hydrogen Consumption ≈ 96.4 ± 3 cc/g | |||
| SURFACE AREA and GAS POROSIMETRY |
Alumina (15 g) | 004-16816-00 | 2000, 2010, 2020, 2100, 2300, 2305,2310, 2360, 2370, 2375, 2380, 2385, 2390, 2400, 2405, 2420, 2600, 2700,2705, 2720, 2750, 2920, 2950, 3000, 3020 |
| Specific Surface Area: | |||
| ≈ 0.5 m2/g; 2360, 2370, 2375, 2380, | |||
| 2385, N2 adsorbate | |||
| ≈ 0.46 m2/g; all others, Kr adsorbate | |||
| Glass Powder (10 g) | 004-16818-00 | ||
| Specific Surface Area ≈ 5.3 m2/g | |||
| Silica Alumina Pellets (10 g) | 004-16821-00 | ||
| Specific Surface Area ≈ 198 m2/g | |||
| Pore Volume ≈ 0.6 cm3/g | |||
| Average Pore Diameter ≈ 115 Å | |||
| Carbon Black (10 g) | 004-16833-00 | ||
| Specific Surface Area ≈ 30.6 m2/g |